EN10219 S235JRH S235J0H S355JRH S355J0H Steel Pipe Pile

Jun 11, 2025

EN 10219 S355J0H is a cold-formed welded structural hollow steel tube in accordance with EN 10219 with a minimum yield strength of 355 MPa (wall thickness ≤ 16 mm) and an impact energy of at least 27 J at 0°C.

The tube is manufactured using electric or submerged arc welding processes without the need for subsequent heat treatment and is suitable for a wide range of building and engineering structural applications, including critical structural components such as piles for foundation support.

Specification

Mechanical Property

steel grade	minimum yield strength Mpa		Tensile strength		Minimum elongation %	Minimum impact energy J
steel grade	Specified thickness mm		Specified thickness mm		Specified thickness mm	at test temperature of
	＜16	＞16≤40	＜3	≥3≤40	≤40	-20℃	0℃	20℃
S235JRH	235	225	360-510	360-510	24	-	-	27
S275J0H	275	265	430-580	410-560	20	-	27	-
S275J2H	275	265	430-580	410-560	20	27	-	-
S355J0H	365	345	510-680	470-630	20	-	27	-
S355J2H						27	-	-
S355K2H						40	-	-

Chemical Composition

Steel grade		Type of de-oxidation a	% by mass, maximum
Steel name	Steel number	C	C	Si	Mn	P	S	Nb
S235JRH	1.0039	FF	0,17	—	1,40	0,040	0,040	0.009
S275J0H	1.0149	FF	0,20	—	1,50	0,035	0,035	0,009
S275J2H	1.0138	FF	0,20	—	1,50	0,030	0,030	—
S355J0H	1.0547	FF	0,22	0,55	1,60	0,035	0,035	0,009
S355J2H	1.0576	FF	0,22	0,55	1,60	0,030	0,030	—
S355K2H	1.0512	FF	0,22	0,55	1,60	0,030	0,030	—
a. The deoxidation method is designated as follows: FF: Fully killed steel containing nitrogen binding elements in amounts sufficient to bind available nitrogen (e.g. min. 0,020 % total Al or 0,015 % soluble Al). b. The maximum value for nitrogen does not apply if the chemical composition shows a minimum total Al content of 0,020 % with a minimum Al/N ratio of 2:1, or if sufficient other N-binding elements are present. The N-binding elements shall be recorded in the Inspection Document.